C93800 Bronze vs. AWS BAg-3

C93800 bronze belongs to the copper alloys classification, while AWS BAg-3 belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is C93800 bronze and the bottom bar is AWS BAg-3.

UNS C93800 (Alloy 3D, SAE 67) Hard Bronze AWS BAg-3 (P07501) Filler Metal

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		96
Elastic (Young's, Tensile) Modulus, GPa		80

Poisson's Ratio		0.35
Poisson's Ratio		0.33

Shear Modulus, GPa		35
Shear Modulus, GPa		30

Tensile Strength: Ultimate (UTS), MPa		200
Tensile Strength: Ultimate (UTS), MPa		170

Thermal Properties

Latent Heat of Fusion, J/g		170
Latent Heat of Fusion, J/g		120

Melting Completion (Liquidus), °C		940
Melting Completion (Liquidus), °C		690

Melting Onset (Solidus), °C		850
Melting Onset (Solidus), °C		630

Specific Heat Capacity, J/kg-K		340
Specific Heat Capacity, J/kg-K		290

Thermal Expansion, µm/m-K		19
Thermal Expansion, µm/m-K		22

Otherwise Unclassified Properties

Density, g/cm³		9.1
Density, g/cm³		9.3

Embodied Carbon, kg CO₂/kg material		3.2
Embodied Carbon, kg CO₂/kg material		49

Embodied Energy, MJ/kg		51
Embodied Energy, MJ/kg		770

Common Calculations

Stiffness to Weight: Axial, points		5.9
Stiffness to Weight: Axial, points		4.8

Stiffness to Weight: Bending, points		17
Stiffness to Weight: Bending, points		15

Strength to Weight: Axial, points		6.1
Strength to Weight: Axial, points		5.1

Strength to Weight: Bending, points		8.4
Strength to Weight: Bending, points		7.3

Thermal Shock Resistance, points		8.1
Thermal Shock Resistance, points		6.9

Alloy Composition

Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452

Aluminum (Al), %		0 to 0.0050
Aluminum (Al), %		0

Antimony (Sb), %		0 to 0.8
Antimony (Sb), %		0

Cadmium (Cd), %		0
Cadmium (Cd), %		15 to 17

Copper (Cu), %		75 to 79
Copper (Cu), %		14.5 to 16.5

Iron (Fe), %		0 to 0.15
Iron (Fe), %		0

Lead (Pb), %		13 to 16
Lead (Pb), %		0

Nickel (Ni), %		0 to 1.0
Nickel (Ni), %		2.5 to 3.5

Phosphorus (P), %		0 to 1.5
Phosphorus (P), %		0

Silicon (Si), %		0 to 0.0050
Silicon (Si), %		0

Silver (Ag), %		0
Silver (Ag), %		49 to 51

Sulfur (S), %		0 to 0.080
Sulfur (S), %		0

Tin (Sn), %		6.3 to 7.5
Tin (Sn), %		0

Zinc (Zn), %		0 to 0.8
Zinc (Zn), %		13.5 to 17.5

Residuals, %		0 to 1.0
Residuals, %		0 to 0.15