C94100 Bronze vs. EN 2.4680 Cast Nickel
C94100 bronze belongs to the copper alloys classification, while EN 2.4680 cast nickel belongs to the nickel alloys. There are 24 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is C94100 bronze and the bottom bar is EN 2.4680 cast nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 92 | |
| 210 |
| Elongation at Break, % | 7.8 | |
| 9.1 |
| Poisson's Ratio | 0.36 | |
| 0.26 |
| Shear Modulus, GPa | 34 | |
| 84 |
| Tensile Strength: Ultimate (UTS), MPa | 190 | |
| 600 |
| Tensile Strength: Yield (Proof), MPa | 130 | |
| 260 |
Thermal Properties
| Latent Heat of Fusion, J/g | 160 | |
| 350 |
| Maximum Temperature: Mechanical, °C | 130 | |
| 1050 |
| Melting Completion (Liquidus), °C | 870 | |
| 1360 |
| Melting Onset (Solidus), °C | 790 | |
| 1320 |
| Specific Heat Capacity, J/kg-K | 330 | |
| 480 |
| Thermal Expansion, µm/m-K | 20 | |
| 15 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 29 | |
| 60 |
| Density, g/cm3 | 9.2 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 3.0 | |
| 9.1 |
| Embodied Energy, MJ/kg | 48 | |
| 130 |
| Embodied Water, L/kg | 370 | |
| 350 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 14 | |
| 45 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 97 | |
| 160 |
| Stiffness to Weight: Axial, points | 5.5 | |
| 15 |
| Stiffness to Weight: Bending, points | 16 | |
| 25 |
| Strength to Weight: Axial, points | 5.8 | |
| 21 |
| Strength to Weight: Bending, points | 8.1 | |
| 20 |
| Thermal Shock Resistance, points | 7.6 | |
| 14 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 to 0.0050 | |
| 0 |
| Antimony (Sb), % | 0 to 0.8 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.1 |
| Chromium (Cr), % | 0 | |
| 48 to 52 |
| Copper (Cu), % | 72 to 79 | |
| 0 |
| Iron (Fe), % | 0 to 0.25 | |
| 0 to 1.0 |
| Lead (Pb), % | 18 to 22 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 0.5 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0 to 1.0 | |
| 42.9 to 51 |
| Niobium (Nb), % | 0 | |
| 1.0 to 1.8 |
| Nitrogen (N), % | 0 | |
| 0 to 0.16 |
| Phosphorus (P), % | 0 to 1.5 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 to 0.0050 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.080 | |
| 0 to 0.020 |
| Tin (Sn), % | 4.5 to 6.5 | |
| 0 |
| Zinc (Zn), % | 0 to 1.0 | |
| 0 |
| Residuals, % | 0 to 1.3 | |
| 0 |