C94300 Bronze vs. C93600 Bronze
Both C94300 bronze and C93600 bronze are copper alloys. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 89% of their average alloy composition in common.
For each property being compared, the top bar is C94300 bronze and the bottom bar is C93600 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 87 | |
| 99 |
| Elongation at Break, % | 9.7 | |
| 14 |
| Poisson's Ratio | 0.36 | |
| 0.35 |
| Shear Modulus, GPa | 32 | |
| 36 |
| Tensile Strength: Ultimate (UTS), MPa | 180 | |
| 260 |
| Tensile Strength: Yield (Proof), MPa | 120 | |
| 140 |
Thermal Properties
| Latent Heat of Fusion, J/g | 150 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 110 | |
| 150 |
| Melting Completion (Liquidus), °C | 820 | |
| 940 |
| Melting Onset (Solidus), °C | 760 | |
| 840 |
| Specific Heat Capacity, J/kg-K | 320 | |
| 350 |
| Thermal Conductivity, W/m-K | 63 | |
| 49 |
| Thermal Expansion, µm/m-K | 20 | |
| 19 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 9.0 | |
| 11 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.7 | |
| 11 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 28 | |
| 31 |
| Density, g/cm3 | 9.3 | |
| 9.0 |
| Embodied Carbon, kg CO2/kg material | 2.9 | |
| 3.2 |
| Embodied Energy, MJ/kg | 47 | |
| 51 |
| Embodied Water, L/kg | 370 | |
| 370 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 15 | |
| 31 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 77 | |
| 98 |
| Stiffness to Weight: Axial, points | 5.2 | |
| 6.1 |
| Stiffness to Weight: Bending, points | 16 | |
| 17 |
| Strength to Weight: Axial, points | 5.2 | |
| 7.9 |
| Strength to Weight: Bending, points | 7.4 | |
| 9.9 |
| Thermal Diffusivity, mm2/s | 21 | |
| 16 |
| Thermal Shock Resistance, points | 7.1 | |
| 9.8 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 to 0.0050 | |
| 0 to 0.0050 |
| Antimony (Sb), % | 0 to 0.8 | |
| 0 to 0.55 |
| Copper (Cu), % | 67 to 72 | |
| 79 to 83 |
| Iron (Fe), % | 0 to 0.15 | |
| 0 to 0.2 |
| Lead (Pb), % | 23 to 27 | |
| 11 to 13 |
| Nickel (Ni), % | 0 to 1.0 | |
| 0 to 1.0 |
| Phosphorus (P), % | 0 to 1.5 | |
| 0 to 1.5 |
| Silicon (Si), % | 0 to 0.0050 | |
| 0 to 0.0050 |
| Sulfur (S), % | 0 to 0.080 | |
| 0 to 0.080 |
| Tin (Sn), % | 4.5 to 6.0 | |
| 6.0 to 8.0 |
| Zinc (Zn), % | 0 to 0.8 | |
| 0 to 1.0 |
| Residuals, % | 0 to 1.0 | |
| 0 to 0.7 |