C95300 Bronze vs. CC752S Brass
Both C95300 bronze and CC752S brass are copper alloys. They have 64% of their average alloy composition in common.
For each property being compared, the top bar is C95300 bronze and the bottom bar is CC752S brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 120 to 170 | |
| 100 |
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 100 |
| Elongation at Break, % | 14 to 25 | |
| 8.4 |
| Poisson's Ratio | 0.34 | |
| 0.31 |
| Shear Modulus, GPa | 42 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 520 to 610 | |
| 350 |
| Tensile Strength: Yield (Proof), MPa | 190 to 310 | |
| 190 |
Thermal Properties
| Latent Heat of Fusion, J/g | 230 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 220 | |
| 130 |
| Melting Completion (Liquidus), °C | 1050 | |
| 840 |
| Melting Onset (Solidus), °C | 1040 | |
| 800 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 380 |
| Thermal Conductivity, W/m-K | 63 | |
| 110 |
| Thermal Expansion, µm/m-K | 18 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 13 | |
| 25 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 14 | |
| 28 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 28 | |
| 24 |
| Density, g/cm3 | 8.3 | |
| 8.1 |
| Embodied Carbon, kg CO2/kg material | 3.1 | |
| 2.7 |
| Embodied Energy, MJ/kg | 52 | |
| 46 |
| Embodied Water, L/kg | 390 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 73 to 100 | |
| 25 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 170 to 420 | |
| 180 |
| Stiffness to Weight: Axial, points | 7.5 | |
| 7.1 |
| Stiffness to Weight: Bending, points | 19 | |
| 19 |
| Strength to Weight: Axial, points | 17 to 21 | |
| 12 |
| Strength to Weight: Bending, points | 17 to 19 | |
| 13 |
| Thermal Diffusivity, mm2/s | 17 | |
| 35 |
| Thermal Shock Resistance, points | 19 to 22 | |
| 12 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 9.0 to 11 | |
| 0.3 to 0.7 |
| Antimony (Sb), % | 0 | |
| 0 to 0.14 |
| Arsenic (As), % | 0 | |
| 0.040 to 0.14 |
| Copper (Cu), % | 86.5 to 90.2 | |
| 61.5 to 64.5 |
| Iron (Fe), % | 0.8 to 1.5 | |
| 0 to 0.3 |
| Lead (Pb), % | 0 | |
| 1.5 to 2.2 |
| Manganese (Mn), % | 0 | |
| 0 to 0.1 |
| Nickel (Ni), % | 0 | |
| 0 to 0.2 |
| Silicon (Si), % | 0 | |
| 0 to 0.020 |
| Tin (Sn), % | 0 | |
| 0 to 0.3 |
| Zinc (Zn), % | 0 | |
| 31.5 to 36.7 |
| Residuals, % | 0 to 1.0 | |
| 0 |