C95300 Bronze vs. C72150 Copper-nickel
Both C95300 bronze and C72150 copper-nickel are copper alloys. They have 55% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is C95300 bronze and the bottom bar is C72150 copper-nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 120 to 170 | |
| 99 |
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 150 |
| Elongation at Break, % | 14 to 25 | |
| 29 |
| Poisson's Ratio | 0.34 | |
| 0.33 |
| Shear Modulus, GPa | 42 | |
| 55 |
| Tensile Strength: Ultimate (UTS), MPa | 520 to 610 | |
| 490 |
| Tensile Strength: Yield (Proof), MPa | 190 to 310 | |
| 210 |
Thermal Properties
| Latent Heat of Fusion, J/g | 230 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 220 | |
| 600 |
| Melting Completion (Liquidus), °C | 1050 | |
| 1210 |
| Melting Onset (Solidus), °C | 1040 | |
| 1250 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 410 |
| Thermal Conductivity, W/m-K | 63 | |
| 22 |
| Thermal Expansion, µm/m-K | 18 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 13 | |
| 3.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 14 | |
| 3.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 28 | |
| 45 |
| Density, g/cm3 | 8.3 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 3.1 | |
| 6.1 |
| Embodied Energy, MJ/kg | 52 | |
| 88 |
| Embodied Water, L/kg | 390 | |
| 270 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 73 to 100 | |
| 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 170 to 420 | |
| 150 |
| Stiffness to Weight: Axial, points | 7.5 | |
| 9.1 |
| Stiffness to Weight: Bending, points | 19 | |
| 20 |
| Strength to Weight: Axial, points | 17 to 21 | |
| 15 |
| Strength to Weight: Bending, points | 17 to 19 | |
| 15 |
| Thermal Diffusivity, mm2/s | 17 | |
| 6.0 |
| Thermal Shock Resistance, points | 19 to 22 | |
| 18 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 9.0 to 11 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.1 |
| Copper (Cu), % | 86.5 to 90.2 | |
| 52.5 to 57 |
| Iron (Fe), % | 0.8 to 1.5 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0 | |
| 0 to 0.050 |
| Nickel (Ni), % | 0 | |
| 43 to 46 |
| Silicon (Si), % | 0 | |
| 0 to 0.5 |
| Zinc (Zn), % | 0 | |
| 0 to 0.2 |
| Residuals, % | 0 to 1.0 | |
| 0 to 0.5 |