C95400 Bronze vs. C70400 Copper-nickel
Both C95400 bronze and C70400 copper-nickel are copper alloys. They have 88% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is C95400 bronze and the bottom bar is C70400 copper-nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 120 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Shear Modulus, GPa | 43 | |
| 45 |
| Tensile Strength: Ultimate (UTS), MPa | 600 to 710 | |
| 300 to 310 |
| Tensile Strength: Yield (Proof), MPa | 240 to 360 | |
| 95 to 230 |
Thermal Properties
| Latent Heat of Fusion, J/g | 230 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 230 | |
| 210 |
| Melting Completion (Liquidus), °C | 1040 | |
| 1120 |
| Melting Onset (Solidus), °C | 1030 | |
| 1060 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 390 |
| Thermal Conductivity, W/m-K | 59 | |
| 64 |
| Thermal Expansion, µm/m-K | 18 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 13 | |
| 14 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 14 | |
| 14 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 27 | |
| 32 |
| Density, g/cm3 | 8.2 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 3.2 | |
| 3.0 |
| Embodied Energy, MJ/kg | 53 | |
| 47 |
| Embodied Water, L/kg | 390 | |
| 300 |
Common Calculations
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 250 to 560 | |
| 38 to 220 |
| Stiffness to Weight: Axial, points | 7.7 | |
| 7.5 |
| Stiffness to Weight: Bending, points | 20 | |
| 19 |
| Strength to Weight: Axial, points | 20 to 24 | |
| 9.3 to 9.8 |
| Strength to Weight: Bending, points | 19 to 22 | |
| 11 to 12 |
| Thermal Diffusivity, mm2/s | 16 | |
| 18 |
| Thermal Shock Resistance, points | 21 to 25 | |
| 10 to 11 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 10 to 11.5 | |
| 0 |
| Copper (Cu), % | 83 to 87 | |
| 89.8 to 93.6 |
| Iron (Fe), % | 3.0 to 5.0 | |
| 1.3 to 1.7 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0.3 to 0.8 |
| Nickel (Ni), % | 0 to 1.5 | |
| 4.8 to 6.2 |
| Zinc (Zn), % | 0 | |
| 0 to 1.0 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.5 |