C96300 Copper-nickel vs. AWS BNi-7
C96300 copper-nickel belongs to the copper alloys classification, while AWS BNi-7 belongs to the nickel alloys. They have a modest 20% of their average alloy composition in common, which, by itself, doesn't mean much. There are 19 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is C96300 copper-nickel and the bottom bar is AWS BNi-7.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 130 | |
| 170 |
| Poisson's Ratio | 0.33 | |
| 0.3 |
| Shear Modulus, GPa | 49 | |
| 67 |
| Tensile Strength: Ultimate (UTS), MPa | 580 | |
| 550 |
Thermal Properties
| Latent Heat of Fusion, J/g | 230 | |
| 280 |
| Melting Completion (Liquidus), °C | 1200 | |
| 890 |
| Melting Onset (Solidus), °C | 1150 | |
| 890 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 490 |
| Thermal Expansion, µm/m-K | 16 | |
| 11 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 42 | |
| 55 |
| Density, g/cm3 | 8.9 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 5.1 | |
| 8.8 |
| Embodied Energy, MJ/kg | 76 | |
| 120 |
| Embodied Water, L/kg | 290 | |
| 240 |
Common Calculations
| Stiffness to Weight: Axial, points | 8.2 | |
| 12 |
| Stiffness to Weight: Bending, points | 19 | |
| 23 |
| Strength to Weight: Axial, points | 18 | |
| 19 |
| Strength to Weight: Bending, points | 17 | |
| 19 |
| Thermal Shock Resistance, points | 20 | |
| 21 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 0 to 0.050 |
| Boron (B), % | 0 | |
| 0 to 0.010 |
| Carbon (C), % | 0 to 0.15 | |
| 0 to 0.060 |
| Chromium (Cr), % | 0 | |
| 13 to 15 |
| Cobalt (Co), % | 0 | |
| 0 to 0.1 |
| Copper (Cu), % | 72.3 to 80.8 | |
| 0 |
| Iron (Fe), % | 0.5 to 1.5 | |
| 0 to 0.2 |
| Lead (Pb), % | 0 to 0.010 | |
| 0 |
| Manganese (Mn), % | 0.25 to 1.5 | |
| 0 to 0.040 |
| Nickel (Ni), % | 18 to 22 | |
| 73.3 to 77.3 |
| Niobium (Nb), % | 0.5 to 1.5 | |
| 0 |
| Phosphorus (P), % | 0 to 0.020 | |
| 9.7 to 10.5 |
| Selenium (Se), % | 0 | |
| 0 to 0.0050 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 to 0.020 |
| Titanium (Ti), % | 0 | |
| 0 to 0.050 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.050 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.5 |