C96300 Copper-nickel vs. AWS E310H
C96300 copper-nickel belongs to the copper alloys classification, while AWS E310H belongs to the iron alloys. They have a modest 23% of their average alloy composition in common, which, by itself, doesn't mean much. There are 24 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is C96300 copper-nickel and the bottom bar is AWS E310H.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 130 | |
| 200 |
| Elongation at Break, % | 11 | |
| 11 |
| Poisson's Ratio | 0.33 | |
| 0.27 |
| Shear Modulus, GPa | 49 | |
| 79 |
| Tensile Strength: Ultimate (UTS), MPa | 580 | |
| 690 |
Thermal Properties
| Latent Heat of Fusion, J/g | 230 | |
| 300 |
| Melting Completion (Liquidus), °C | 1200 | |
| 1400 |
| Melting Onset (Solidus), °C | 1150 | |
| 1350 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 480 |
| Thermal Conductivity, W/m-K | 37 | |
| 14 |
| Thermal Expansion, µm/m-K | 16 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 6.0 | |
| 2.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 6.1 | |
| 2.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 42 | |
| 26 |
| Density, g/cm3 | 8.9 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 5.1 | |
| 4.6 |
| Embodied Energy, MJ/kg | 76 | |
| 65 |
| Embodied Water, L/kg | 290 | |
| 200 |
Common Calculations
| Stiffness to Weight: Axial, points | 8.2 | |
| 14 |
| Stiffness to Weight: Bending, points | 19 | |
| 25 |
| Strength to Weight: Axial, points | 18 | |
| 25 |
| Strength to Weight: Bending, points | 17 | |
| 22 |
| Thermal Diffusivity, mm2/s | 10 | |
| 3.8 |
| Thermal Shock Resistance, points | 20 | |
| 17 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Carbon (C), % | 0 to 0.15 | |
| 0.35 to 0.45 |
| Chromium (Cr), % | 0 | |
| 25 to 28 |
| Copper (Cu), % | 72.3 to 80.8 | |
| 0 to 0.75 |
| Iron (Fe), % | 0.5 to 1.5 | |
| 44.2 to 53.7 |
| Lead (Pb), % | 0 to 0.010 | |
| 0 |
| Manganese (Mn), % | 0.25 to 1.5 | |
| 1.0 to 2.5 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.75 |
| Nickel (Ni), % | 18 to 22 | |
| 20 to 22.5 |
| Niobium (Nb), % | 0.5 to 1.5 | |
| 0 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.75 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 to 0.030 |
| Residuals, % | 0 to 0.5 | |
| 0 |