MakeItFrom.com
Menu (ESC)

C96300 Copper-nickel vs. CC330G Bronze

Both C96300 copper-nickel and CC330G bronze are copper alloys. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 78% of their average alloy composition in common.

For each property being compared, the top bar is C96300 copper-nickel and the bottom bar is CC330G bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
110
Elastic (Young's, Tensile) Modulus, GPa 130
110
Elongation at Break, % 11
20
Poisson's Ratio 0.33
0.34
Shear Modulus, GPa 49
42
Tensile Strength: Ultimate (UTS), MPa 580
530
Tensile Strength: Yield (Proof), MPa 430
190

Thermal Properties

Latent Heat of Fusion, J/g 230
230
Maximum Temperature: Mechanical, °C 240
220
Melting Completion (Liquidus), °C 1200
1050
Melting Onset (Solidus), °C 1150
1000
Specific Heat Capacity, J/kg-K 400
430
Thermal Conductivity, W/m-K 37
62
Thermal Expansion, µm/m-K 16
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 6.0
14
Electrical Conductivity: Equal Weight (Specific), % IACS 6.1
15

Otherwise Unclassified Properties

Base Metal Price, % relative 42
29
Density, g/cm3 8.9
8.4
Embodied Carbon, kg CO2/kg material 5.1
3.2
Embodied Energy, MJ/kg 76
52
Embodied Water, L/kg 290
390

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 59
82
Resilience: Unit (Modulus of Resilience), kJ/m3 720
170
Stiffness to Weight: Axial, points 8.2
7.5
Stiffness to Weight: Bending, points 19
19
Strength to Weight: Axial, points 18
18
Strength to Weight: Bending, points 17
17
Thermal Diffusivity, mm2/s 10
17
Thermal Shock Resistance, points 20
19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
8.0 to 10.5
Carbon (C), % 0 to 0.15
0
Copper (Cu), % 72.3 to 80.8
87 to 92
Iron (Fe), % 0.5 to 1.5
0 to 1.2
Lead (Pb), % 0 to 0.010
0 to 0.3
Manganese (Mn), % 0.25 to 1.5
0 to 0.5
Nickel (Ni), % 18 to 22
0 to 1.0
Niobium (Nb), % 0.5 to 1.5
0
Phosphorus (P), % 0 to 0.020
0
Silicon (Si), % 0 to 0.5
0 to 0.2
Sulfur (S), % 0 to 0.020
0
Tin (Sn), % 0
0 to 0.3
Zinc (Zn), % 0
0 to 0.5
Residuals, % 0 to 0.5
0