C96300 Copper-nickel vs. C95400 Bronze

Both C96300 copper-nickel and C95400 bronze are copper alloys. They have 79% of their average alloy composition in common.

For each property being compared, the top bar is C96300 copper-nickel and the bottom bar is C95400 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
160 to 200
Elastic (Young's, Tensile) Modulus, GPa 130
110
Elongation at Break, % 11
8.1 to 16
Poisson's Ratio 0.33
0.34
Shear Modulus, GPa 49
43
Tensile Strength: Ultimate (UTS), MPa 580
600 to 710
Tensile Strength: Yield (Proof), MPa 430
240 to 360

Thermal Properties

Latent Heat of Fusion, J/g 230
230
Maximum Temperature: Mechanical, °C 240
230
Melting Completion (Liquidus), °C 1200
1040
Melting Onset (Solidus), °C 1150
1030
Specific Heat Capacity, J/kg-K 400
440
Thermal Conductivity, W/m-K 37
59
Thermal Expansion, µm/m-K 16
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 6.0
13
Electrical Conductivity: Equal Weight (Specific), % IACS 6.1
14

Otherwise Unclassified Properties

Base Metal Price, % relative 42
27
Density, g/cm3 8.9
8.2
Embodied Carbon, kg CO2/kg material 5.1
3.2
Embodied Energy, MJ/kg 76
53
Embodied Water, L/kg 290
390

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 59
48 to 75
Resilience: Unit (Modulus of Resilience), kJ/m3 720
250 to 560
Stiffness to Weight: Axial, points 8.2
7.7
Stiffness to Weight: Bending, points 19
20
Strength to Weight: Axial, points 18
20 to 24
Strength to Weight: Bending, points 17
19 to 22
Thermal Diffusivity, mm2/s 10
16
Thermal Shock Resistance, points 20
21 to 25

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
10 to 11.5
Carbon (C), % 0 to 0.15
0
Copper (Cu), % 72.3 to 80.8
83 to 87
Iron (Fe), % 0.5 to 1.5
3.0 to 5.0
Lead (Pb), % 0 to 0.010
0
Manganese (Mn), % 0.25 to 1.5
0 to 0.5
Nickel (Ni), % 18 to 22
0 to 1.5
Niobium (Nb), % 0.5 to 1.5
0
Phosphorus (P), % 0 to 0.020
0
Silicon (Si), % 0 to 0.5
0
Sulfur (S), % 0 to 0.020
0
Residuals, % 0 to 0.5
0 to 0.5