C96400 Copper-nickel vs. EN 1.5521 Steel
C96400 copper-nickel belongs to the copper alloys classification, while EN 1.5521 steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is C96400 copper-nickel and the bottom bar is EN 1.5521 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 190 |
| Elongation at Break, % | 25 | |
| 11 to 21 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 51 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 490 | |
| 430 to 1390 |
| Tensile Strength: Yield (Proof), MPa | 260 | |
| 300 to 490 |
Thermal Properties
| Latent Heat of Fusion, J/g | 240 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 260 | |
| 400 |
| Melting Completion (Liquidus), °C | 1240 | |
| 1460 |
| Melting Onset (Solidus), °C | 1170 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 470 |
| Thermal Conductivity, W/m-K | 28 | |
| 51 |
| Thermal Expansion, µm/m-K | 15 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 5.0 | |
| 7.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 5.1 | |
| 8.1 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 45 | |
| 1.9 |
| Density, g/cm3 | 8.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 5.9 | |
| 1.4 |
| Embodied Energy, MJ/kg | 87 | |
| 19 |
| Embodied Water, L/kg | 280 | |
| 47 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 100 | |
| 44 to 230 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 250 | |
| 250 to 630 |
| Stiffness to Weight: Axial, points | 8.6 | |
| 13 |
| Stiffness to Weight: Bending, points | 19 | |
| 24 |
| Strength to Weight: Axial, points | 15 | |
| 15 to 49 |
| Strength to Weight: Bending, points | 16 | |
| 16 to 35 |
| Thermal Diffusivity, mm2/s | 7.8 | |
| 14 |
| Thermal Shock Resistance, points | 17 | |
| 13 to 41 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Boron (B), % | 0 | |
| 0.00080 to 0.0050 |
| Carbon (C), % | 0 to 0.15 | |
| 0.16 to 0.2 |
| Copper (Cu), % | 62.3 to 71.3 | |
| 0 to 0.25 |
| Iron (Fe), % | 0.25 to 1.5 | |
| 98 to 98.9 |
| Lead (Pb), % | 0 to 0.010 | |
| 0 |
| Manganese (Mn), % | 0 to 1.5 | |
| 0.9 to 1.2 |
| Nickel (Ni), % | 28 to 32 | |
| 0 |
| Niobium (Nb), % | 0.5 to 1.5 | |
| 0 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.3 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 to 0.025 |
| Residuals, % | 0 to 0.5 | |
| 0 |