C96600 Copper vs. EN 1.7102 Steel
C96600 copper belongs to the copper alloys classification, while EN 1.7102 steel belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is C96600 copper and the bottom bar is EN 1.7102 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 190 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 52 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 760 | |
| 670 to 2010 |
Thermal Properties
| Latent Heat of Fusion, J/g | 240 | |
| 270 |
| Maximum Temperature: Mechanical, °C | 280 | |
| 410 |
| Melting Completion (Liquidus), °C | 1180 | |
| 1440 |
| Melting Onset (Solidus), °C | 1100 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 480 |
| Thermal Conductivity, W/m-K | 30 | |
| 47 |
| Thermal Expansion, µm/m-K | 15 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 4.0 | |
| 7.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 4.1 | |
| 8.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 65 | |
| 2.2 |
| Density, g/cm3 | 8.9 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 7.0 | |
| 1.5 |
| Embodied Energy, MJ/kg | 100 | |
| 20 |
| Embodied Water, L/kg | 280 | |
| 48 |
Common Calculations
| Stiffness to Weight: Axial, points | 8.7 | |
| 13 |
| Stiffness to Weight: Bending, points | 20 | |
| 25 |
| Strength to Weight: Axial, points | 24 | |
| 24 to 72 |
| Strength to Weight: Bending, points | 21 | |
| 22 to 46 |
| Thermal Diffusivity, mm2/s | 8.4 | |
| 13 |
| Thermal Shock Resistance, points | 25 | |
| 20 to 60 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Beryllium (Be), % | 0.4 to 0.7 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.51 to 0.59 |
| Chromium (Cr), % | 0 | |
| 0.5 to 0.8 |
| Copper (Cu), % | 63.5 to 69.8 | |
| 0 |
| Iron (Fe), % | 0.8 to 1.1 | |
| 96.2 to 97.3 |
| Lead (Pb), % | 0 to 0.010 | |
| 0 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0.5 to 0.8 |
| Nickel (Ni), % | 29 to 33 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.15 | |
| 1.2 to 1.6 |
| Sulfur (S), % | 0 | |
| 0 to 0.025 |
| Residuals, % | 0 to 0.5 | |
| 0 |