C96700 Copper vs. AWS E2595
C96700 copper belongs to the copper alloys classification, while AWS E2595 belongs to the iron alloys. There are 22 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is C96700 copper and the bottom bar is AWS E2595.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 200 |
| Elongation at Break, % | 10 | |
| 17 |
| Poisson's Ratio | 0.33 | |
| 0.27 |
| Shear Modulus, GPa | 53 | |
| 80 |
| Tensile Strength: Ultimate (UTS), MPa | 1210 | |
| 850 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 300 |
| Melting Completion (Liquidus), °C | 1170 | |
| 1450 |
| Melting Onset (Solidus), °C | 1110 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 470 |
| Thermal Conductivity, W/m-K | 30 | |
| 16 |
| Thermal Expansion, µm/m-K | 15 | |
| 14 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 90 | |
| 23 |
| Density, g/cm3 | 8.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 9.5 | |
| 4.4 |
| Embodied Energy, MJ/kg | 140 | |
| 61 |
| Embodied Water, L/kg | 280 | |
| 190 |
Common Calculations
| Stiffness to Weight: Axial, points | 8.9 | |
| 14 |
| Stiffness to Weight: Bending, points | 20 | |
| 25 |
| Strength to Weight: Axial, points | 38 | |
| 30 |
| Strength to Weight: Bending, points | 29 | |
| 25 |
| Thermal Diffusivity, mm2/s | 8.5 | |
| 4.2 |
| Thermal Shock Resistance, points | 40 | |
| 21 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Beryllium (Be), % | 1.1 to 1.2 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.040 |
| Chromium (Cr), % | 0 | |
| 24 to 27 |
| Copper (Cu), % | 62.4 to 68.8 | |
| 0.4 to 1.5 |
| Iron (Fe), % | 0.4 to 1.0 | |
| 51.4 to 64.5 |
| Lead (Pb), % | 0 to 0.010 | |
| 0 |
| Manganese (Mn), % | 0.4 to 1.0 | |
| 0 to 2.5 |
| Molybdenum (Mo), % | 0 | |
| 2.5 to 4.5 |
| Nickel (Ni), % | 29 to 33 | |
| 8.0 to 10.5 |
| Nitrogen (N), % | 0 | |
| 0.2 to 0.3 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.15 | |
| 0 to 1.2 |
| Sulfur (S), % | 0 | |
| 0 to 0.025 |
| Titanium (Ti), % | 0.15 to 0.35 | |
| 0 |
| Tungsten (W), % | 0 | |
| 0.4 to 1.0 |
| Zirconium (Zr), % | 0.15 to 0.35 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |