C96900 Copper-nickel vs. C95300 Bronze
Both C96900 copper-nickel and C95300 bronze are copper alloys. They have 76% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is C96900 copper-nickel and the bottom bar is C95300 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 110 |
| Elongation at Break, % | 4.5 | |
| 14 to 25 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Shear Modulus, GPa | 45 | |
| 42 |
| Tensile Strength: Ultimate (UTS), MPa | 850 | |
| 520 to 610 |
| Tensile Strength: Yield (Proof), MPa | 830 | |
| 190 to 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 230 |
| Maximum Temperature: Mechanical, °C | 210 | |
| 220 |
| Melting Completion (Liquidus), °C | 1060 | |
| 1050 |
| Melting Onset (Solidus), °C | 960 | |
| 1040 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 440 |
| Thermal Expansion, µm/m-K | 17 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 9.0 | |
| 13 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 9.2 | |
| 14 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 39 | |
| 28 |
| Density, g/cm3 | 8.8 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 4.6 | |
| 3.1 |
| Embodied Energy, MJ/kg | 72 | |
| 52 |
| Embodied Water, L/kg | 360 | |
| 390 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 38 | |
| 73 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2820 | |
| 170 to 420 |
| Stiffness to Weight: Axial, points | 7.7 | |
| 7.5 |
| Stiffness to Weight: Bending, points | 19 | |
| 19 |
| Strength to Weight: Axial, points | 27 | |
| 17 to 21 |
| Strength to Weight: Bending, points | 23 | |
| 17 to 19 |
| Thermal Shock Resistance, points | 30 | |
| 19 to 22 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 9.0 to 11 |
| Copper (Cu), % | 73.6 to 78 | |
| 86.5 to 90.2 |
| Iron (Fe), % | 0 to 0.5 | |
| 0.8 to 1.5 |
| Lead (Pb), % | 0 to 0.020 | |
| 0 |
| Magnesium (Mg), % | 0 to 0.15 | |
| 0 |
| Manganese (Mn), % | 0.050 to 0.3 | |
| 0 |
| Nickel (Ni), % | 14.5 to 15.5 | |
| 0 |
| Niobium (Nb), % | 0 to 0.1 | |
| 0 |
| Silicon (Si), % | 0 to 0.3 | |
| 0 |
| Tin (Sn), % | 7.5 to 8.5 | |
| 0 |
| Zinc (Zn), % | 0 to 0.5 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 to 1.0 |