C97600 Dairy Metal vs. 359.0 Aluminum
C97600 dairy metal belongs to the copper alloys classification, while 359.0 aluminum belongs to the aluminum alloys. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is C97600 dairy metal and the bottom bar is 359.0 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 71 |
| Elongation at Break, % | 11 | |
| 3.8 to 4.9 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 46 | |
| 27 |
| Tensile Strength: Ultimate (UTS), MPa | 310 | |
| 340 to 350 |
| Tensile Strength: Yield (Proof), MPa | 140 | |
| 250 to 280 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 530 |
| Maximum Temperature: Mechanical, °C | 210 | |
| 170 |
| Melting Completion (Liquidus), °C | 1140 | |
| 600 |
| Melting Onset (Solidus), °C | 1110 | |
| 570 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 910 |
| Thermal Conductivity, W/m-K | 22 | |
| 140 |
| Thermal Expansion, µm/m-K | 17 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 5.0 | |
| 35 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 5.1 | |
| 120 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 37 | |
| 9.5 |
| Density, g/cm3 | 8.8 | |
| 2.6 |
| Embodied Carbon, kg CO2/kg material | 4.6 | |
| 8.0 |
| Embodied Energy, MJ/kg | 69 | |
| 150 |
| Embodied Water, L/kg | 330 | |
| 1090 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 29 | |
| 12 to 15 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 85 | |
| 450 to 540 |
| Stiffness to Weight: Axial, points | 7.7 | |
| 15 |
| Stiffness to Weight: Bending, points | 19 | |
| 54 |
| Strength to Weight: Axial, points | 9.8 | |
| 37 to 38 |
| Strength to Weight: Bending, points | 12 | |
| 42 to 43 |
| Thermal Diffusivity, mm2/s | 6.5 | |
| 59 |
| Thermal Shock Resistance, points | 11 | |
| 16 to 17 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 to 0.0050 | |
| 88.9 to 91 |
| Antimony (Sb), % | 0 to 0.25 | |
| 0 |
| Copper (Cu), % | 63 to 67 | |
| 0 to 0.2 |
| Iron (Fe), % | 0 to 1.5 | |
| 0 to 0.2 |
| Lead (Pb), % | 3.0 to 5.0 | |
| 0 |
| Magnesium (Mg), % | 0 | |
| 0.5 to 0.7 |
| Manganese (Mn), % | 0 | |
| 0 to 0.1 |
| Nickel (Ni), % | 19 to 21.5 | |
| 0 |
| Phosphorus (P), % | 0 to 0.050 | |
| 0 |
| Silicon (Si), % | 0 to 0.15 | |
| 8.5 to 9.5 |
| Sulfur (S), % | 0 to 0.080 | |
| 0 |
| Tin (Sn), % | 3.5 to 4.0 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0 to 0.2 |
| Zinc (Zn), % | 3.0 to 9.0 | |
| 0 to 0.1 |
| Residuals, % | 0 to 0.3 | |
| 0 to 0.15 |