C97600 Dairy Metal vs. AISI 201 Stainless Steel
C97600 dairy metal belongs to the copper alloys classification, while AISI 201 stainless steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is C97600 dairy metal and the bottom bar is AISI 201 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 200 |
| Elongation at Break, % | 11 | |
| 4.6 to 51 |
| Poisson's Ratio | 0.33 | |
| 0.28 |
| Shear Modulus, GPa | 46 | |
| 77 |
| Tensile Strength: Ultimate (UTS), MPa | 310 | |
| 650 to 1450 |
| Tensile Strength: Yield (Proof), MPa | 140 | |
| 300 to 1080 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 280 |
| Maximum Temperature: Mechanical, °C | 210 | |
| 880 |
| Melting Completion (Liquidus), °C | 1140 | |
| 1410 |
| Melting Onset (Solidus), °C | 1110 | |
| 1370 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 480 |
| Thermal Conductivity, W/m-K | 22 | |
| 15 |
| Thermal Expansion, µm/m-K | 17 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 5.0 | |
| 2.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 5.1 | |
| 2.9 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 37 | |
| 12 |
| Density, g/cm3 | 8.8 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 4.6 | |
| 2.6 |
| Embodied Energy, MJ/kg | 69 | |
| 38 |
| Embodied Water, L/kg | 330 | |
| 140 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 29 | |
| 61 to 340 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 85 | |
| 230 to 2970 |
| Stiffness to Weight: Axial, points | 7.7 | |
| 14 |
| Stiffness to Weight: Bending, points | 19 | |
| 25 |
| Strength to Weight: Axial, points | 9.8 | |
| 23 to 52 |
| Strength to Weight: Bending, points | 12 | |
| 22 to 37 |
| Thermal Diffusivity, mm2/s | 6.5 | |
| 4.0 |
| Thermal Shock Resistance, points | 11 | |
| 14 to 32 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 to 0.0050 | |
| 0 |
| Antimony (Sb), % | 0 to 0.25 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.15 |
| Chromium (Cr), % | 0 | |
| 16 to 18 |
| Copper (Cu), % | 63 to 67 | |
| 0 |
| Iron (Fe), % | 0 to 1.5 | |
| 67.5 to 75 |
| Lead (Pb), % | 3.0 to 5.0 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 5.5 to 7.5 |
| Nickel (Ni), % | 19 to 21.5 | |
| 3.5 to 5.5 |
| Nitrogen (N), % | 0 | |
| 0 to 0.25 |
| Phosphorus (P), % | 0 to 0.050 | |
| 0 to 0.060 |
| Silicon (Si), % | 0 to 0.15 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.080 | |
| 0 to 0.030 |
| Tin (Sn), % | 3.5 to 4.0 | |
| 0 |
| Zinc (Zn), % | 3.0 to 9.0 | |
| 0 |
| Residuals, % | 0 to 0.3 | |
| 0 |