C97600 Dairy Metal vs. Z13004 Zinc
C97600 dairy metal belongs to the copper alloys classification, while Z13004 zinc belongs to the zinc alloys.
For each property being compared, the top bar is C97600 dairy metal and the bottom bar is Z13004 zinc.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 87 |
| Elongation at Break, % | 11 | |
| 30 |
| Poisson's Ratio | 0.33 | |
| 0.25 |
| Shear Modulus, GPa | 46 | |
| 35 |
| Tensile Strength: Ultimate (UTS), MPa | 310 | |
| 93 |
| Tensile Strength: Yield (Proof), MPa | 140 | |
| 76 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 110 |
| Maximum Temperature: Mechanical, °C | 210 | |
| 90 |
| Melting Completion (Liquidus), °C | 1140 | |
| 410 |
| Melting Onset (Solidus), °C | 1110 | |
| 390 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 390 |
| Thermal Conductivity, W/m-K | 22 | |
| 110 |
| Thermal Expansion, µm/m-K | 17 | |
| 26 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 5.0 | |
| 27 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 5.1 | |
| 37 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 37 | |
| 11 |
| Density, g/cm3 | 8.8 | |
| 6.6 |
| Embodied Carbon, kg CO2/kg material | 4.6 | |
| 2.8 |
| Embodied Energy, MJ/kg | 69 | |
| 53 |
| Embodied Water, L/kg | 330 | |
| 340 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 29 | |
| 26 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 85 | |
| 33 |
| Stiffness to Weight: Axial, points | 7.7 | |
| 7.4 |
| Stiffness to Weight: Bending, points | 19 | |
| 23 |
| Strength to Weight: Axial, points | 9.8 | |
| 3.9 |
| Strength to Weight: Bending, points | 12 | |
| 7.0 |
| Thermal Diffusivity, mm2/s | 6.5 | |
| 44 |
| Thermal Shock Resistance, points | 11 | |
| 2.9 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 to 0.0050 | |
| 0 to 0.0020 |
| Antimony (Sb), % | 0 to 0.25 | |
| 0 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0030 |
| Copper (Cu), % | 63 to 67 | |
| 0 to 0.0030 |
| Iron (Fe), % | 0 to 1.5 | |
| 0 to 0.0030 |
| Lead (Pb), % | 3.0 to 5.0 | |
| 0 to 0.0030 |
| Nickel (Ni), % | 19 to 21.5 | |
| 0 |
| Phosphorus (P), % | 0 to 0.050 | |
| 0 |
| Silicon (Si), % | 0 to 0.15 | |
| 0 |
| Sulfur (S), % | 0 to 0.080 | |
| 0 |
| Tin (Sn), % | 3.5 to 4.0 | |
| 0 to 0.0010 |
| Zinc (Zn), % | 3.0 to 9.0 | |
| 99.985 to 100 |
| Residuals, % | 0 to 0.3 | |
| 0 |