C97600 Dairy Metal vs. C87900 Brass
Both C97600 dairy metal and C87900 brass are copper alloys. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 72% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is C97600 dairy metal and the bottom bar is C87900 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 110 |
| Elongation at Break, % | 11 | |
| 25 |
| Poisson's Ratio | 0.33 | |
| 0.31 |
| Shear Modulus, GPa | 46 | |
| 41 |
| Tensile Strength: Ultimate (UTS), MPa | 310 | |
| 480 |
| Tensile Strength: Yield (Proof), MPa | 140 | |
| 240 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 190 |
| Maximum Temperature: Mechanical, °C | 210 | |
| 130 |
| Melting Completion (Liquidus), °C | 1140 | |
| 930 |
| Melting Onset (Solidus), °C | 1110 | |
| 900 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 390 |
| Thermal Conductivity, W/m-K | 22 | |
| 120 |
| Thermal Expansion, µm/m-K | 17 | |
| 20 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 5.0 | |
| 15 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 5.1 | |
| 17 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 37 | |
| 24 |
| Density, g/cm3 | 8.8 | |
| 8.1 |
| Embodied Carbon, kg CO2/kg material | 4.6 | |
| 2.7 |
| Embodied Energy, MJ/kg | 69 | |
| 46 |
| Embodied Water, L/kg | 330 | |
| 320 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 29 | |
| 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 85 | |
| 270 |
| Stiffness to Weight: Axial, points | 7.7 | |
| 7.3 |
| Stiffness to Weight: Bending, points | 19 | |
| 20 |
| Strength to Weight: Axial, points | 9.8 | |
| 17 |
| Strength to Weight: Bending, points | 12 | |
| 17 |
| Thermal Diffusivity, mm2/s | 6.5 | |
| 37 |
| Thermal Shock Resistance, points | 11 | |
| 16 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 to 0.0050 | |
| 0 to 0.15 |
| Antimony (Sb), % | 0 to 0.25 | |
| 0 to 0.050 |
| Arsenic (As), % | 0 | |
| 0 to 0.050 |
| Copper (Cu), % | 63 to 67 | |
| 63 to 69.2 |
| Iron (Fe), % | 0 to 1.5 | |
| 0 to 0.4 |
| Lead (Pb), % | 3.0 to 5.0 | |
| 0 to 0.25 |
| Manganese (Mn), % | 0 | |
| 0 to 0.15 |
| Nickel (Ni), % | 19 to 21.5 | |
| 0 to 0.5 |
| Phosphorus (P), % | 0 to 0.050 | |
| 0 to 0.010 |
| Silicon (Si), % | 0 to 0.15 | |
| 0.8 to 1.2 |
| Sulfur (S), % | 0 to 0.080 | |
| 0 to 0.050 |
| Tin (Sn), % | 3.5 to 4.0 | |
| 0 to 0.25 |
| Zinc (Zn), % | 3.0 to 9.0 | |
| 30 to 36 |
| Residuals, % | 0 to 0.3 | |
| 0 |