C99700 Brass vs. EN 1.7380 Steel
C99700 brass belongs to the copper alloys classification, while EN 1.7380 steel belongs to the iron alloys. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is C99700 brass and the bottom bar is EN 1.7380 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 190 |
| Elongation at Break, % | 25 | |
| 19 to 20 |
| Poisson's Ratio | 0.32 | |
| 0.29 |
| Shear Modulus, GPa | 46 | |
| 74 |
| Tensile Strength: Ultimate (UTS), MPa | 380 | |
| 540 to 550 |
| Tensile Strength: Yield (Proof), MPa | 170 | |
| 290 to 330 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 260 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 460 |
| Melting Completion (Liquidus), °C | 900 | |
| 1470 |
| Melting Onset (Solidus), °C | 880 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 410 | |
| 470 |
| Thermal Expansion, µm/m-K | 20 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 3.0 | |
| 7.6 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.3 | |
| 8.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 25 | |
| 3.8 |
| Density, g/cm3 | 8.1 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 3.3 | |
| 1.8 |
| Embodied Energy, MJ/kg | 53 | |
| 23 |
| Embodied Water, L/kg | 320 | |
| 59 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 78 | |
| 87 to 98 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 120 | |
| 230 to 280 |
| Stiffness to Weight: Axial, points | 8.3 | |
| 13 |
| Stiffness to Weight: Bending, points | 20 | |
| 24 |
| Strength to Weight: Axial, points | 13 | |
| 19 to 20 |
| Strength to Weight: Bending, points | 14 | |
| 19 |
| Thermal Shock Resistance, points | 11 | |
| 15 to 16 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0.5 to 3.0 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.080 to 0.14 |
| Chromium (Cr), % | 0 | |
| 2.0 to 2.5 |
| Copper (Cu), % | 54 to 65.5 | |
| 0 to 0.3 |
| Iron (Fe), % | 0 to 1.0 | |
| 94.6 to 96.6 |
| Lead (Pb), % | 0 to 2.0 | |
| 0 |
| Manganese (Mn), % | 11 to 15 | |
| 0.4 to 0.8 |
| Molybdenum (Mo), % | 0 | |
| 0.9 to 1.1 |
| Nickel (Ni), % | 4.0 to 6.0 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.012 |
| Phosphorus (P), % | 0 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 | |
| 0 to 0.010 |
| Tin (Sn), % | 0 to 1.0 | |
| 0 |
| Zinc (Zn), % | 19 to 25 | |
| 0 |
| Residuals, % | 0 to 0.3 | |
| 0 |