C99700 Brass vs. N06060 Nickel
C99700 brass belongs to the copper alloys classification, while N06060 nickel belongs to the nickel alloys. There are 24 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is C99700 brass and the bottom bar is N06060 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 210 |
| Elongation at Break, % | 25 | |
| 45 |
| Poisson's Ratio | 0.32 | |
| 0.29 |
| Shear Modulus, GPa | 46 | |
| 82 |
| Tensile Strength: Ultimate (UTS), MPa | 380 | |
| 700 |
| Tensile Strength: Yield (Proof), MPa | 170 | |
| 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 320 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 980 |
| Melting Completion (Liquidus), °C | 900 | |
| 1510 |
| Melting Onset (Solidus), °C | 880 | |
| 1450 |
| Specific Heat Capacity, J/kg-K | 410 | |
| 430 |
| Thermal Expansion, µm/m-K | 20 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 25 | |
| 65 |
| Density, g/cm3 | 8.1 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 3.3 | |
| 12 |
| Embodied Energy, MJ/kg | 53 | |
| 160 |
| Embodied Water, L/kg | 320 | |
| 280 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 78 | |
| 250 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 120 | |
| 180 |
| Stiffness to Weight: Axial, points | 8.3 | |
| 14 |
| Stiffness to Weight: Bending, points | 20 | |
| 23 |
| Strength to Weight: Axial, points | 13 | |
| 22 |
| Strength to Weight: Bending, points | 14 | |
| 20 |
| Thermal Shock Resistance, points | 11 | |
| 19 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0.5 to 3.0 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.030 |
| Chromium (Cr), % | 0 | |
| 19 to 22 |
| Copper (Cu), % | 54 to 65.5 | |
| 0.25 to 1.3 |
| Iron (Fe), % | 0 to 1.0 | |
| 0 to 14 |
| Lead (Pb), % | 0 to 2.0 | |
| 0 |
| Manganese (Mn), % | 11 to 15 | |
| 0 to 1.5 |
| Molybdenum (Mo), % | 0 | |
| 12 to 14 |
| Nickel (Ni), % | 4.0 to 6.0 | |
| 54 to 60 |
| Niobium (Nb), % | 0 | |
| 0.5 to 1.3 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 | |
| 0 to 0.0050 |
| Tin (Sn), % | 0 to 1.0 | |
| 0 |
| Tungsten (W), % | 0 | |
| 0.25 to 1.3 |
| Zinc (Zn), % | 19 to 25 | |
| 0 |
| Residuals, % | 0 to 0.3 | |
| 0 |