C99700 Brass vs. R30021 Cobalt
C99700 brass belongs to the copper alloys classification, while R30021 cobalt belongs to the cobalt alloys. There are 24 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is C99700 brass and the bottom bar is R30021 cobalt.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 220 |
| Elongation at Break, % | 25 | |
| 9.0 |
| Poisson's Ratio | 0.32 | |
| 0.29 |
| Shear Modulus, GPa | 46 | |
| 86 |
| Tensile Strength: Ultimate (UTS), MPa | 380 | |
| 700 |
| Tensile Strength: Yield (Proof), MPa | 170 | |
| 500 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 330 |
| Melting Completion (Liquidus), °C | 900 | |
| 1350 |
| Melting Onset (Solidus), °C | 880 | |
| 1190 |
| Specific Heat Capacity, J/kg-K | 410 | |
| 450 |
| Thermal Expansion, µm/m-K | 20 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 3.0 | |
| 1.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.3 | |
| 2.1 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.1 | |
| 8.4 |
| Embodied Carbon, kg CO2/kg material | 3.3 | |
| 8.0 |
| Embodied Energy, MJ/kg | 53 | |
| 110 |
| Embodied Water, L/kg | 320 | |
| 520 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 78 | |
| 57 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 120 | |
| 570 |
| Stiffness to Weight: Axial, points | 8.3 | |
| 15 |
| Stiffness to Weight: Bending, points | 20 | |
| 24 |
| Strength to Weight: Axial, points | 13 | |
| 23 |
| Strength to Weight: Bending, points | 14 | |
| 21 |
| Thermal Shock Resistance, points | 11 | |
| 21 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0.5 to 3.0 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.2 to 0.35 |
| Chromium (Cr), % | 0 | |
| 26 to 29 |
| Cobalt (Co), % | 0 | |
| 61.7 to 67.3 |
| Copper (Cu), % | 54 to 65.5 | |
| 0 |
| Iron (Fe), % | 0 to 1.0 | |
| 0 to 3.0 |
| Lead (Pb), % | 0 to 2.0 | |
| 0 |
| Manganese (Mn), % | 11 to 15 | |
| 0 |
| Molybdenum (Mo), % | 0 | |
| 4.5 to 6.0 |
| Nickel (Ni), % | 4.0 to 6.0 | |
| 2.0 to 3.0 |
| Silicon (Si), % | 0 | |
| 0 to 1.5 |
| Tin (Sn), % | 0 to 1.0 | |
| 0 |
| Zinc (Zn), % | 19 to 25 | |
| 0 |
| Residuals, % | 0 to 0.3 | |
| 0 |