C99750 Brass vs. C67600 Bronze
Both C99750 brass and C67600 bronze are copper alloys. They have 80% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is C99750 brass and the bottom bar is C67600 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 130 | |
| 100 |
| Elongation at Break, % | 20 to 30 | |
| 13 to 33 |
| Poisson's Ratio | 0.32 | |
| 0.31 |
| Shear Modulus, GPa | 48 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 450 to 520 | |
| 430 to 570 |
| Tensile Strength: Yield (Proof), MPa | 220 to 280 | |
| 170 to 380 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 120 |
| Melting Completion (Liquidus), °C | 840 | |
| 890 |
| Melting Onset (Solidus), °C | 820 | |
| 870 |
| Specific Heat Capacity, J/kg-K | 410 | |
| 380 |
| Thermal Expansion, µm/m-K | 20 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.0 | |
| 24 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.2 | |
| 27 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 23 | |
| 23 |
| Density, g/cm3 | 8.1 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 3.1 | |
| 2.8 |
| Embodied Energy, MJ/kg | 51 | |
| 47 |
| Embodied Water, L/kg | 310 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 87 to 110 | |
| 63 to 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 190 to 300 | |
| 140 to 680 |
| Stiffness to Weight: Axial, points | 8.6 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 21 | |
| 20 |
| Strength to Weight: Axial, points | 15 to 18 | |
| 15 to 20 |
| Strength to Weight: Bending, points | 16 to 18 | |
| 16 to 19 |
| Thermal Shock Resistance, points | 13 to 15 | |
| 14 to 19 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0.25 to 3.0 | |
| 0 |
| Copper (Cu), % | 55 to 61 | |
| 57 to 60 |
| Iron (Fe), % | 0 to 1.0 | |
| 0.4 to 1.3 |
| Lead (Pb), % | 0.5 to 2.5 | |
| 0.5 to 1.0 |
| Manganese (Mn), % | 17 to 23 | |
| 0.050 to 0.5 |
| Nickel (Ni), % | 0 to 5.0 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0.5 to 1.5 |
| Zinc (Zn), % | 17 to 23 | |
| 35.2 to 41.6 |
| Residuals, % | 0 to 0.3 | |
| 0 to 0.5 |