K93050 Alloy vs. ASTM A202 Steel

Both K93050 alloy and ASTM A202 steel are iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is K93050 alloy and the bottom bar is ASTM A202 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.3
0.29
Shear Modulus, GPa 72
73
Tensile Strength: Ultimate (UTS), MPa 500 to 680
590 to 670

Thermal Properties

Latent Heat of Fusion, J/g 270
260
Melting Completion (Liquidus), °C 1430
1450
Melting Onset (Solidus), °C 1380
1410
Specific Heat Capacity, J/kg-K 460
470
Thermal Expansion, µm/m-K 12
13

Otherwise Unclassified Properties

Base Metal Price, % relative 26
2.1
Density, g/cm3 8.2
7.8
Embodied Carbon, kg CO2/kg material 4.7
1.4
Embodied Energy, MJ/kg 65
19
Embodied Water, L/kg 120
49

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 17 to 23
21 to 24
Strength to Weight: Bending, points 17 to 21
20 to 22
Thermal Shock Resistance, points 16 to 21
17 to 20

Comparable Variants