K93600 Alloy vs. 90-silver 10-tin-oxide
K93600 alloy belongs to the iron alloys classification, while 90-silver 10-tin-oxide belongs to the otherwise unclassified metals. There are 6 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.
For each property being compared, the top bar is K93600 alloy and the bottom bar is 90-silver 10-tin-oxide.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
| 77 to 82 |
| Elongation at Break, % | 5.0 to 35 | |
| 7.0 to 35 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 21 to 280 | |
| 20 to 68 |
| Shear Strength, MPa | 320 to 380 | |
| 160 to 170 |
| Tensile Strength: Ultimate (UTS), MPa | 480 to 810 | |
| 230 to 300 |
| Tensile Strength: Yield (Proof), MPa | 280 to 750 | |
| 120 to 280 |