K93600 Alloy vs. ACI-ASTM CA6NM Steel

Both K93600 alloy and ACI-ASTM CA6NM steel are iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is K93600 alloy and the bottom bar is ACI-ASTM CA6NM steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 140
200
Elongation at Break, % 5.0 to 35
17
Tensile Strength: Ultimate (UTS), MPa 480 to 810
850
Tensile Strength: Yield (Proof), MPa 280 to 750
620

Thermal Properties

Maximum Temperature: Mechanical, °C 440
770
Melting Onset (Solidus), °C 1430
1400
Specific Heat Capacity, J/kg-K 520
480
Thermal Conductivity, W/m-K 13
25
Thermal Expansion, µm/m-K 7.3
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.8
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
3.2

Otherwise Unclassified Properties

Density, g/cm3 8.1
7.8

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 21 to 280
130
Resilience: Unit (Modulus of Resilience), kJ/m3 280 to 2050
1000
Stiffness to Weight: Axial, points 9.4
14
Stiffness to Weight: Bending, points 21
25
Strength to Weight: Axial, points 16 to 28
30
Strength to Weight: Bending, points 17 to 24
26
Thermal Diffusivity, mm2/s 3.1
6.7
Thermal Shock Resistance, points 34 to 57
31