K93600 Alloy vs. ACI-ASTM CB7Cu-1 Steel

Both K93600 alloy and ACI-ASTM CB7Cu-1 steel are iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is K93600 alloy and the bottom bar is ACI-ASTM CB7Cu-1 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 140
190
Elongation at Break, % 5.0 to 35
5.7 to 11
Tensile Strength: Ultimate (UTS), MPa 480 to 810
960 to 1350
Tensile Strength: Yield (Proof), MPa 280 to 750
760 to 1180

Thermal Properties

Melting Onset (Solidus), °C 1430
1500
Specific Heat Capacity, J/kg-K 520
480
Thermal Conductivity, W/m-K 13
17
Thermal Expansion, µm/m-K 7.3
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.3

Otherwise Unclassified Properties

Density, g/cm3 8.1
7.8

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 21 to 280
71 to 120
Resilience: Unit (Modulus of Resilience), kJ/m3 280 to 2050
1500 to 3590
Stiffness to Weight: Axial, points 9.4
14
Stiffness to Weight: Bending, points 21
25
Strength to Weight: Axial, points 16 to 28
34 to 48
Strength to Weight: Bending, points 17 to 24
28 to 35
Thermal Diffusivity, mm2/s 3.1
4.6
Thermal Shock Resistance, points 34 to 57
32 to 45