K93600 Alloy vs. ACI-ASTM CF16Fa Steel

Both K93600 alloy and ACI-ASTM CF16Fa steel are iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is K93600 alloy and the bottom bar is ACI-ASTM CF16Fa steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 140
200
Elongation at Break, % 5.0 to 35
28
Tensile Strength: Ultimate (UTS), MPa 480 to 810
540
Tensile Strength: Yield (Proof), MPa 280 to 750
230

Thermal Properties

Maximum Temperature: Mechanical, °C 440
980
Melting Onset (Solidus), °C 1430
1370
Specific Heat Capacity, J/kg-K 520
480
Thermal Conductivity, W/m-K 13
16
Thermal Expansion, µm/m-K 7.3
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.4

Otherwise Unclassified Properties

Density, g/cm3 8.1
7.8

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 21 to 280
120
Resilience: Unit (Modulus of Resilience), kJ/m3 280 to 2050
140
Stiffness to Weight: Axial, points 9.4
14
Stiffness to Weight: Bending, points 21
25
Strength to Weight: Axial, points 16 to 28
19
Strength to Weight: Bending, points 17 to 24
19
Thermal Diffusivity, mm2/s 3.1
4.2
Thermal Shock Resistance, points 34 to 57
12