K93600 Alloy vs. ACI-ASTM CT15C Steel

Both K93600 alloy and ACI-ASTM CT15C steel are iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is K93600 alloy and the bottom bar is ACI-ASTM CT15C steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 140
200
Elongation at Break, % 5.0 to 35
23
Tensile Strength: Ultimate (UTS), MPa 480 to 810
500
Tensile Strength: Yield (Proof), MPa 280 to 750
190

Thermal Properties

Maximum Temperature: Mechanical, °C 440
1080
Melting Onset (Solidus), °C 1430
1360
Specific Heat Capacity, J/kg-K 520
470
Thermal Conductivity, W/m-K 13
12
Thermal Expansion, µm/m-K 7.3
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
1.9

Otherwise Unclassified Properties

Density, g/cm3 8.1
8.0

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 21 to 280
90
Resilience: Unit (Modulus of Resilience), kJ/m3 280 to 2050
93
Stiffness to Weight: Axial, points 9.4
14
Stiffness to Weight: Bending, points 21
24
Strength to Weight: Axial, points 16 to 28
17
Strength to Weight: Bending, points 17 to 24
17
Thermal Diffusivity, mm2/s 3.1
3.2
Thermal Shock Resistance, points 34 to 57
12