K93600 Alloy vs. AISI 205 Stainless Steel
Both K93600 alloy and AISI 205 stainless steel are iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is K93600 alloy and the bottom bar is AISI 205 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 140 | |
200 |
Elongation at Break, % | 5.0 to 35 | |
11 to 51 |
Shear Strength, MPa | 320 to 380 | |
560 to 850 |
Tensile Strength: Ultimate (UTS), MPa | 480 to 810 | |
800 to 1430 |
Tensile Strength: Yield (Proof), MPa | 280 to 750 | |
450 to 1100 |
Thermal Properties
Maximum Temperature: Mechanical, °C | 440 | |
880 |
Melting Onset (Solidus), °C | 1430 | |
1340 |
Specific Heat Capacity, J/kg-K | 520 | |
480 |
Thermal Expansion, µm/m-K | 7.3 | |
18 |
Otherwise Unclassified Properties
Density, g/cm3 | 8.1 | |
7.6 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 21 to 280 | |
150 to 430 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 280 to 2050 | |
510 to 3060 |
Stiffness to Weight: Axial, points | 9.4 | |
14 |
Stiffness to Weight: Bending, points | 21 | |
26 |
Strength to Weight: Axial, points | 16 to 28 | |
29 to 52 |
Strength to Weight: Bending, points | 17 to 24 | |
25 to 37 |
Thermal Shock Resistance, points | 34 to 57 | |
16 to 29 |