K93600 Alloy vs. AISI 309Cb Stainless Steel

Both K93600 alloy and AISI 309Cb stainless steel are iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is K93600 alloy and the bottom bar is AISI 309Cb stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 140
200
Elongation at Break, % 5.0 to 35
39
Shear Strength, MPa 320 to 380
390
Tensile Strength: Ultimate (UTS), MPa 480 to 810
580
Tensile Strength: Yield (Proof), MPa 280 to 750
230

Thermal Properties

Maximum Temperature: Mechanical, °C 440
1090
Melting Onset (Solidus), °C 1430
1380
Specific Heat Capacity, J/kg-K 520
480
Thermal Conductivity, W/m-K 13
15
Thermal Expansion, µm/m-K 7.3
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.5

Otherwise Unclassified Properties

Density, g/cm3 8.1
7.8

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 21 to 280
180
Resilience: Unit (Modulus of Resilience), kJ/m3 280 to 2050
140
Stiffness to Weight: Axial, points 9.4
14
Stiffness to Weight: Bending, points 21
25
Strength to Weight: Axial, points 16 to 28
20
Strength to Weight: Bending, points 17 to 24
20
Thermal Diffusivity, mm2/s 3.1
4.0
Thermal Shock Resistance, points 34 to 57
13