K93600 Alloy vs. ASTM A148 Cast Steel
Both K93600 alloy and ASTM A148 cast steel are iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is K93600 alloy and the bottom bar is ASTM A148 cast steel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 140 | |
190 |
Elongation at Break, % | 5.0 to 35 | |
5.7 to 25 |
Tensile Strength: Ultimate (UTS), MPa | 480 to 810 | |
630 to 1300 |
Tensile Strength: Yield (Proof), MPa | 280 to 750 | |
390 to 1160 |
Thermal Properties
Maximum Temperature: Mechanical, °C | 440 | |
400 to 430 |
Melting Onset (Solidus), °C | 1430 | |
1420 |
Specific Heat Capacity, J/kg-K | 520 | |
470 |
Thermal Conductivity, W/m-K | 13 | |
37 to 47 |
Thermal Expansion, µm/m-K | 7.3 | |
13 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
7.3 to 7.5 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 2.4 | |
8.3 to 8.6 |
Otherwise Unclassified Properties
Density, g/cm3 | 8.1 | |
7.8 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 21 to 280 | |
71 to 150 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 280 to 2050 | |
400 to 3570 |
Stiffness to Weight: Axial, points | 9.4 | |
13 |
Stiffness to Weight: Bending, points | 21 | |
24 |
Strength to Weight: Axial, points | 16 to 28 | |
22 to 46 |
Strength to Weight: Bending, points | 17 to 24 | |
21 to 34 |
Thermal Diffusivity, mm2/s | 3.1 | |
9.9 to 13 |
Thermal Shock Resistance, points | 34 to 57 | |
18 to 38 |