K93600 Alloy vs. ASTM A209 Steel
Both K93600 alloy and ASTM A209 steel are iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is K93600 alloy and the bottom bar is ASTM A209 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 190 |
| Elongation at Break, % | 5.0 to 35 | |
| 34 |
| Shear Strength, MPa | 320 to 380 | |
| 280 to 310 |
| Tensile Strength: Ultimate (UTS), MPa | 480 to 810 | |
| 420 to 460 |
| Tensile Strength: Yield (Proof), MPa | 280 to 750 | |
| 220 to 250 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 440 | |
| 410 |
| Melting Onset (Solidus), °C | 1430 | |
| 1420 to 1430 |
| Specific Heat Capacity, J/kg-K | 520 | |
| 470 |
| Thermal Conductivity, W/m-K | 13 | |
| 50 |
| Thermal Expansion, µm/m-K | 7.3 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
| 7.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.4 | |
| 8.1 to 8.2 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.1 | |
| 7.9 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 21 to 280 | |
| 120 to 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 280 to 2050 | |
| 130 to 170 |
| Stiffness to Weight: Axial, points | 9.4 | |
| 13 |
| Stiffness to Weight: Bending, points | 21 | |
| 24 |
| Strength to Weight: Axial, points | 16 to 28 | |
| 15 to 16 |
| Strength to Weight: Bending, points | 17 to 24 | |
| 16 to 17 |
| Thermal Diffusivity, mm2/s | 3.1 | |
| 13 |
| Thermal Shock Resistance, points | 34 to 57 | |
| 12 to 14 |