K93600 Alloy vs. ASTM A217 Cast Steel
Both K93600 alloy and ASTM A217 cast steel are iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is K93600 alloy and the bottom bar is ASTM A217 cast steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 190 |
| Elongation at Break, % | 5.0 to 35 | |
| 21 to 27 |
| Tensile Strength: Ultimate (UTS), MPa | 480 to 810 | |
| 540 to 710 |
| Tensile Strength: Yield (Proof), MPa | 280 to 750 | |
| 270 to 460 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 440 | |
| 410 to 600 |
| Melting Onset (Solidus), °C | 1430 | |
| 1410 to 1420 |
| Specific Heat Capacity, J/kg-K | 520 | |
| 470 |
| Thermal Conductivity, W/m-K | 13 | |
| 26 to 50 |
| Thermal Expansion, µm/m-K | 7.3 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
| 7.3 to 9.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.4 | |
| 8.4 to 11 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.1 | |
| 7.8 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 21 to 280 | |
| 110 to 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 280 to 2050 | |
| 190 to 570 |
| Stiffness to Weight: Axial, points | 9.4 | |
| 13 to 14 |
| Stiffness to Weight: Bending, points | 21 | |
| 24 to 25 |
| Strength to Weight: Axial, points | 16 to 28 | |
| 19 to 25 |
| Strength to Weight: Bending, points | 17 to 24 | |
| 19 to 23 |
| Thermal Diffusivity, mm2/s | 3.1 | |
| 6.9 to 14 |
| Thermal Shock Resistance, points | 34 to 57 | |
| 16 to 20 |