K93600 Alloy vs. ASTM B631 Class C
K93600 alloy belongs to the iron alloys classification, while ASTM B631 class C belongs to the otherwise unclassified metals. There are 10 material properties with values for both materials. Properties with values for just one material (19, in this case) are not shown.
For each property being compared, the top bar is K93600 alloy and the bottom bar is ASTM B631 class C.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 8.1 | |
| 13 to 14 |
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 180 to 190 |
| Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
| 55 to 63 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.4 | |
| 36 to 43 |
| Specific Heat Capacity, J/kg-K | 520 | |
| 180 |
| Stiffness to Weight: Axial, points | 9.4 | |
| 7.4 to 7.6 |
| Stiffness to Weight: Bending, points | 21 | |
| 14 |
| Thermal Conductivity, W/m-K | 13 | |
| 450 to 490 |
| Thermal Diffusivity, mm2/s | 3.1 | |
| 180 to 200 |
| Thermal Expansion, µm/m-K | 7.3 | |
| 14 |