K93600 Alloy vs. ASTM B685 Alloy
K93600 alloy belongs to the iron alloys classification, while ASTM B685 alloy belongs to the otherwise unclassified metals. There are 13 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is K93600 alloy and the bottom bar is ASTM B685 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 120 |
| Tensile Strength: Ultimate (UTS), MPa | 480 to 810 | |
| 660 to 1060 |
Thermal Properties
| Melting Onset (Solidus), °C | 1430 | |
| 1200 |
| Specific Heat Capacity, J/kg-K | 520 | |
| 300 |
| Thermal Expansion, µm/m-K | 7.3 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
| 5.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.4 | |
| 4.1 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.1 | |
| 11 |
Common Calculations
| Stiffness to Weight: Axial, points | 9.4 | |
| 6.1 |
| Stiffness to Weight: Bending, points | 21 | |
| 15 |
| Strength to Weight: Axial, points | 16 to 28 | |
| 17 to 27 |
| Strength to Weight: Bending, points | 17 to 24 | |
| 16 to 21 |
| Thermal Shock Resistance, points | 34 to 57 | |
| 28 to 46 |