K93600 Alloy vs. AWS ERNiCr-3
K93600 alloy belongs to the iron alloys classification, while AWS ERNiCr-3 belongs to the nickel alloys. There are 12 material properties with values for both materials. Properties with values for just one material (18, in this case) are not shown.
For each property being compared, the top bar is K93600 alloy and the bottom bar is AWS ERNiCr-3.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 140 | |
190 |
Elongation at Break, % | 5.0 to 35 | |
34 |
Tensile Strength: Ultimate (UTS), MPa | 480 to 810 | |
630 |
Thermal Properties
Melting Onset (Solidus), °C | 1430 | |
1330 |
Specific Heat Capacity, J/kg-K | 520 | |
460 |
Thermal Expansion, µm/m-K | 7.3 | |
13 |
Otherwise Unclassified Properties
Density, g/cm3 | 8.1 | |
8.4 |
Common Calculations
Stiffness to Weight: Axial, points | 9.4 | |
13 |
Stiffness to Weight: Bending, points | 21 | |
23 |
Strength to Weight: Axial, points | 16 to 28 | |
21 |
Strength to Weight: Bending, points | 17 to 24 | |
19 |
Thermal Shock Resistance, points | 34 to 57 | |
18 |