K93600 Alloy vs. AWS ERNiCrMo-2
K93600 alloy belongs to the iron alloys classification, while AWS ERNiCrMo-2 belongs to the nickel alloys. There are 15 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is K93600 alloy and the bottom bar is AWS ERNiCrMo-2.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 210 |
| Tensile Strength: Ultimate (UTS), MPa | 480 to 810 | |
| 750 |
Thermal Properties
| Melting Onset (Solidus), °C | 1430 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 520 | |
| 450 |
| Thermal Conductivity, W/m-K | 13 | |
| 11 |
| Thermal Expansion, µm/m-K | 7.3 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
| 1.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.4 | |
| 1.6 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.1 | |
| 8.4 |
Common Calculations
| Stiffness to Weight: Axial, points | 9.4 | |
| 14 |
| Stiffness to Weight: Bending, points | 21 | |
| 23 |
| Strength to Weight: Axial, points | 16 to 28 | |
| 25 |
| Strength to Weight: Bending, points | 17 to 24 | |
| 22 |
| Thermal Diffusivity, mm2/s | 3.1 | |
| 2.9 |
| Thermal Shock Resistance, points | 34 to 57 | |
| 20 |