K93600 Alloy vs. Austempered Cast Iron
Both K93600 alloy and austempered cast iron are iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is K93600 alloy and the bottom bar is austempered cast iron.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 180 |
| Elongation at Break, % | 5.0 to 35 | |
| 1.1 to 13 |
| Tensile Strength: Ultimate (UTS), MPa | 480 to 810 | |
| 860 to 1800 |
| Tensile Strength: Yield (Proof), MPa | 280 to 750 | |
| 560 to 1460 |
Thermal Properties
| Melting Onset (Solidus), °C | 1430 | |
| 1340 |
| Specific Heat Capacity, J/kg-K | 520 | |
| 490 |
| Thermal Conductivity, W/m-K | 13 | |
| 42 |
| Thermal Expansion, µm/m-K | 7.3 | |
| 13 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.1 | |
| 7.5 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 21 to 280 | |
| 19 to 95 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 280 to 2050 | |
| 880 to 3970 |
| Stiffness to Weight: Axial, points | 9.4 | |
| 13 |
| Stiffness to Weight: Bending, points | 21 | |
| 25 |
| Strength to Weight: Axial, points | 16 to 28 | |
| 32 to 66 |
| Strength to Weight: Bending, points | 17 to 24 | |
| 27 to 44 |
| Thermal Diffusivity, mm2/s | 3.1 | |
| 11 |
| Thermal Shock Resistance, points | 34 to 57 | |
| 25 to 53 |