Both K93600 alloy and EN 1.0558 cast steel are iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is K93600 alloy and the bottom bar is EN 1.0558 cast steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 140
190
Elongation at Break, % 5.0 to 35
18
Tensile Strength: Ultimate (UTS), MPa 480 to 810
640
Tensile Strength: Yield (Proof), MPa 280 to 750
340

Thermal Properties

Maximum Temperature: Mechanical, °C 440
400
Melting Onset (Solidus), °C 1430
1430
Specific Heat Capacity, J/kg-K 520
470
Thermal Conductivity, W/m-K 13
53
Thermal Expansion, µm/m-K 7.3
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.8
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.9

Otherwise Unclassified Properties

Density, g/cm3 8.1
7.9

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 21 to 280
99
Resilience: Unit (Modulus of Resilience), kJ/m3 280 to 2050
300
Stiffness to Weight: Axial, points 9.4
13
Stiffness to Weight: Bending, points 21
24
Strength to Weight: Axial, points 16 to 28
22
Strength to Weight: Bending, points 17 to 24
21
Thermal Diffusivity, mm2/s 3.1
14
Thermal Shock Resistance, points 34 to 57
20