K93600 Alloy vs. EN 1.3537 Steel
Both K93600 alloy and EN 1.3537 steel are iron alloys. There are 16 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.
For each property being compared, the top bar is K93600 alloy and the bottom bar is EN 1.3537 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 190 |
| Tensile Strength: Ultimate (UTS), MPa | 480 to 810 | |
| 620 to 730 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 440 | |
| 440 |
| Melting Onset (Solidus), °C | 1430 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 520 | |
| 470 |
| Thermal Conductivity, W/m-K | 13 | |
| 43 |
| Thermal Expansion, µm/m-K | 7.3 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
| 7.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.4 | |
| 8.5 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.1 | |
| 7.8 |
Common Calculations
| Stiffness to Weight: Axial, points | 9.4 | |
| 13 |
| Stiffness to Weight: Bending, points | 21 | |
| 24 |
| Strength to Weight: Axial, points | 16 to 28 | |
| 22 to 26 |
| Strength to Weight: Bending, points | 17 to 24 | |
| 21 to 23 |
| Thermal Diffusivity, mm2/s | 3.1 | |
| 12 |
| Thermal Shock Resistance, points | 34 to 57 | |
| 18 to 22 |