K93600 Alloy vs. EN 1.4104 Stainless Steel
Both K93600 alloy and EN 1.4104 stainless steel are iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is K93600 alloy and the bottom bar is EN 1.4104 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 140 | |
200 |
Elongation at Break, % | 5.0 to 35 | |
11 to 23 |
Shear Strength, MPa | 320 to 380 | |
400 to 450 |
Tensile Strength: Ultimate (UTS), MPa | 480 to 810 | |
630 to 750 |
Tensile Strength: Yield (Proof), MPa | 280 to 750 | |
350 to 560 |
Thermal Properties
Maximum Temperature: Mechanical, °C | 440 | |
860 |
Melting Onset (Solidus), °C | 1430 | |
1390 |
Specific Heat Capacity, J/kg-K | 520 | |
480 |
Thermal Conductivity, W/m-K | 13 | |
25 |
Thermal Expansion, µm/m-K | 7.3 | |
10 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
2.5 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 2.4 | |
2.9 |
Otherwise Unclassified Properties
Density, g/cm3 | 8.1 | |
7.7 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 21 to 280 | |
77 to 120 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 280 to 2050 | |
310 to 800 |
Stiffness to Weight: Axial, points | 9.4 | |
14 |
Stiffness to Weight: Bending, points | 21 | |
25 |
Strength to Weight: Axial, points | 16 to 28 | |
23 to 27 |
Strength to Weight: Bending, points | 17 to 24 | |
21 to 24 |
Thermal Diffusivity, mm2/s | 3.1 | |
6.7 |
Thermal Shock Resistance, points | 34 to 57 | |
22 to 27 |