K93600 Alloy vs. EN 1.4107 Stainless Steel
Both K93600 alloy and EN 1.4107 stainless steel are iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is K93600 alloy and the bottom bar is EN 1.4107 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 140 | |
190 |
Elongation at Break, % | 5.0 to 35 | |
18 to 21 |
Tensile Strength: Ultimate (UTS), MPa | 480 to 810 | |
620 to 700 |
Tensile Strength: Yield (Proof), MPa | 280 to 750 | |
400 to 570 |
Thermal Properties
Maximum Temperature: Mechanical, °C | 440 | |
740 |
Melting Onset (Solidus), °C | 1430 | |
1410 |
Specific Heat Capacity, J/kg-K | 520 | |
480 |
Thermal Conductivity, W/m-K | 13 | |
27 |
Thermal Expansion, µm/m-K | 7.3 | |
10 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
2.9 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 2.4 | |
3.3 |
Otherwise Unclassified Properties
Density, g/cm3 | 8.1 | |
7.8 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 21 to 280 | |
110 to 120 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 280 to 2050 | |
420 to 840 |
Stiffness to Weight: Axial, points | 9.4 | |
14 |
Stiffness to Weight: Bending, points | 21 | |
25 |
Strength to Weight: Axial, points | 16 to 28 | |
22 to 25 |
Strength to Weight: Bending, points | 17 to 24 | |
21 to 22 |
Thermal Diffusivity, mm2/s | 3.1 | |
7.2 |
Thermal Shock Resistance, points | 34 to 57 | |
22 to 25 |