K93600 Alloy vs. EN 1.4301 Stainless Steel

Both K93600 alloy and EN 1.4301 stainless steel are iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is K93600 alloy and the bottom bar is EN 1.4301 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 140
200
Elongation at Break, % 5.0 to 35
14 to 46
Shear Strength, MPa 320 to 380
430 to 550
Tensile Strength: Ultimate (UTS), MPa 480 to 810
610 to 900
Tensile Strength: Yield (Proof), MPa 280 to 750
220 to 570

Thermal Properties

Maximum Temperature: Mechanical, °C 440
940
Melting Onset (Solidus), °C 1430
1380
Specific Heat Capacity, J/kg-K 520
480
Thermal Conductivity, W/m-K 13
15
Thermal Expansion, µm/m-K 7.3
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.7

Otherwise Unclassified Properties

Density, g/cm3 8.1
7.8

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 21 to 280
110 to 220
Resilience: Unit (Modulus of Resilience), kJ/m3 280 to 2050
120 to 820
Stiffness to Weight: Axial, points 9.4
14
Stiffness to Weight: Bending, points 21
25
Strength to Weight: Axial, points 16 to 28
22 to 32
Strength to Weight: Bending, points 17 to 24
20 to 27
Thermal Diffusivity, mm2/s 3.1
4.0
Thermal Shock Resistance, points 34 to 57
14 to 20

Comparable Variants