K93600 Alloy vs. EN 1.4612 Stainless Steel
Both K93600 alloy and EN 1.4612 stainless steel are iron alloys. There are 16 material properties with values for both materials. Properties with values for just one material (18, in this case) are not shown.
For each property being compared, the top bar is K93600 alloy and the bottom bar is EN 1.4612 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 140 | |
190 |
Elongation at Break, % | 5.0 to 35 | |
11 |
Shear Strength, MPa | 320 to 380 | |
1010 to 1110 |
Tensile Strength: Ultimate (UTS), MPa | 480 to 810 | |
1690 to 1850 |
Tensile Strength: Yield (Proof), MPa | 280 to 750 | |
1570 to 1730 |
Thermal Properties
Maximum Temperature: Mechanical, °C | 440 | |
790 |
Melting Onset (Solidus), °C | 1430 | |
1400 |
Specific Heat Capacity, J/kg-K | 520 | |
480 |
Thermal Expansion, µm/m-K | 7.3 | |
11 |
Otherwise Unclassified Properties
Density, g/cm3 | 8.1 | |
7.9 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 21 to 280 | |
190 to 210 |
Stiffness to Weight: Axial, points | 9.4 | |
14 |
Stiffness to Weight: Bending, points | 21 | |
25 |
Strength to Weight: Axial, points | 16 to 28 | |
60 to 65 |
Strength to Weight: Bending, points | 17 to 24 | |
40 to 43 |
Thermal Shock Resistance, points | 34 to 57 | |
58 to 63 |