K93600 Alloy vs. EN 1.4849 Stainless Steel

Both K93600 alloy and EN 1.4849 stainless steel are iron alloys. There are 18 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.

For each property being compared, the top bar is K93600 alloy and the bottom bar is EN 1.4849 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 140
190
Elongation at Break, % 5.0 to 35
4.5
Tensile Strength: Ultimate (UTS), MPa 480 to 810
480
Tensile Strength: Yield (Proof), MPa 280 to 750
250

Thermal Properties

Maximum Temperature: Mechanical, °C 440
1020
Melting Onset (Solidus), °C 1430
1340
Specific Heat Capacity, J/kg-K 520
480
Thermal Conductivity, W/m-K 13
12
Thermal Expansion, µm/m-K 7.3
15

Otherwise Unclassified Properties

Density, g/cm3 8.1
8.0

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 21 to 280
18
Resilience: Unit (Modulus of Resilience), kJ/m3 280 to 2050
160
Stiffness to Weight: Axial, points 9.4
13
Stiffness to Weight: Bending, points 21
24
Strength to Weight: Axial, points 16 to 28
17
Strength to Weight: Bending, points 17 to 24
17
Thermal Diffusivity, mm2/s 3.1
3.2
Thermal Shock Resistance, points 34 to 57
11