K93600 Alloy vs. EN 1.4874 Stainless Steel

Both K93600 alloy and EN 1.4874 stainless steel are iron alloys. There are 18 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.

For each property being compared, the top bar is K93600 alloy and the bottom bar is EN 1.4874 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 140
210
Elongation at Break, % 5.0 to 35
6.7
Tensile Strength: Ultimate (UTS), MPa 480 to 810
480
Tensile Strength: Yield (Proof), MPa 280 to 750
360

Thermal Properties

Maximum Temperature: Mechanical, °C 440
1150
Melting Onset (Solidus), °C 1430
1400
Specific Heat Capacity, J/kg-K 520
450
Thermal Conductivity, W/m-K 13
13
Thermal Expansion, µm/m-K 7.3
15

Otherwise Unclassified Properties

Density, g/cm3 8.1
8.4

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 21 to 280
29
Resilience: Unit (Modulus of Resilience), kJ/m3 280 to 2050
310
Stiffness to Weight: Axial, points 9.4
14
Stiffness to Weight: Bending, points 21
24
Strength to Weight: Axial, points 16 to 28
16
Strength to Weight: Bending, points 17 to 24
16
Thermal Diffusivity, mm2/s 3.1
3.3
Thermal Shock Resistance, points 34 to 57
11