K93600 Alloy vs. EN 1.4962 Stainless Steel

Both K93600 alloy and EN 1.4962 stainless steel are iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is K93600 alloy and the bottom bar is EN 1.4962 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 140
200
Elongation at Break, % 5.0 to 35
22 to 34
Shear Strength, MPa 320 to 380
420 to 440
Tensile Strength: Ultimate (UTS), MPa 480 to 810
630 to 690
Tensile Strength: Yield (Proof), MPa 280 to 750
260 to 490

Thermal Properties

Maximum Temperature: Mechanical, °C 440
910
Melting Onset (Solidus), °C 1430
1440
Specific Heat Capacity, J/kg-K 520
470
Thermal Conductivity, W/m-K 13
14
Thermal Expansion, µm/m-K 7.3
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.6

Otherwise Unclassified Properties

Density, g/cm3 8.1
8.1

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 21 to 280
140 to 170
Resilience: Unit (Modulus of Resilience), kJ/m3 280 to 2050
170 to 610
Stiffness to Weight: Axial, points 9.4
14
Stiffness to Weight: Bending, points 21
24
Strength to Weight: Axial, points 16 to 28
21 to 24
Strength to Weight: Bending, points 17 to 24
20 to 21
Thermal Diffusivity, mm2/s 3.1
3.7
Thermal Shock Resistance, points 34 to 57
14 to 16