MakeItFrom.com
Menu (ESC)

K93600 Alloy vs. EN 1.5113 Steel

Both K93600 alloy and EN 1.5113 steel are iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is K93600 alloy and the bottom bar is EN 1.5113 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 140
190
Elongation at Break, % 5.0 to 35
11 to 18
Shear Strength, MPa 320 to 380
360 to 540
Tensile Strength: Ultimate (UTS), MPa 480 to 810
580 to 900
Tensile Strength: Yield (Proof), MPa 280 to 750
320 to 770

Thermal Properties

Maximum Temperature: Mechanical, °C 440
400
Melting Onset (Solidus), °C 1430
1410
Specific Heat Capacity, J/kg-K 520
480
Thermal Conductivity, W/m-K 13
52
Thermal Expansion, µm/m-K 7.3
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.4

Otherwise Unclassified Properties

Density, g/cm3 8.1
7.8

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 21 to 280
91 to 96
Resilience: Unit (Modulus of Resilience), kJ/m3 280 to 2050
270 to 1570
Stiffness to Weight: Axial, points 9.4
13
Stiffness to Weight: Bending, points 21
24
Strength to Weight: Axial, points 16 to 28
21 to 32
Strength to Weight: Bending, points 17 to 24
20 to 27
Thermal Diffusivity, mm2/s 3.1
14
Thermal Shock Resistance, points 34 to 57
17 to 26