K93600 Alloy vs. Grade 15 Babbitt Metal
K93600 alloy belongs to the iron alloys classification, while grade 15 Babbitt Metal belongs to the otherwise unclassified metals. There are 7 material properties with values for both materials. Properties with values for just one material (24, in this case) are not shown.
For each property being compared, the top bar is K93600 alloy and the bottom bar is grade 15 Babbitt Metal.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 8.1 | |
| 10 |
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 23 |
| Melting Onset (Solidus), °C | 1430 | |
| 250 |
| Specific Heat Capacity, J/kg-K | 520 | |
| 140 |
| Stiffness to Weight: Axial, points | 9.4 | |
| 1.2 |
| Stiffness to Weight: Bending, points | 21 | |
| 9.0 |
| Thermal Expansion, µm/m-K | 7.3 | |
| 26 |