K93600 Alloy vs. Grade 300 Maraging Steel
Both K93600 alloy and grade 300 maraging steel are iron alloys. There are 15 material properties with values for both materials. Properties with values for just one material (18, in this case) are not shown.
For each property being compared, the top bar is K93600 alloy and the bottom bar is grade 300 maraging steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 190 |
| Elongation at Break, % | 5.0 to 35 | |
| 6.5 to 18 |
| Shear Strength, MPa | 320 to 380 | |
| 640 to 1190 |
| Tensile Strength: Ultimate (UTS), MPa | 480 to 810 | |
| 1030 to 2030 |
| Tensile Strength: Yield (Proof), MPa | 280 to 750 | |
| 760 to 1990 |
Thermal Properties
| Melting Onset (Solidus), °C | 1430 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 520 | |
| 450 |
| Thermal Expansion, µm/m-K | 7.3 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.1 | |
| 8.2 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 21 to 280 | |
| 130 to 170 |
| Stiffness to Weight: Axial, points | 9.4 | |
| 13 |
| Stiffness to Weight: Bending, points | 21 | |
| 23 |
| Strength to Weight: Axial, points | 16 to 28 | |
| 35 to 68 |
| Strength to Weight: Bending, points | 17 to 24 | |
| 28 to 43 |
| Thermal Shock Resistance, points | 34 to 57 | |
| 31 to 62 |